Evaluation of the Resilient Modulus of Hot-Mix Asphalt Made With Recycled Concrete Aggregates From Construction and Demolition Waste
Ver/ abrir
Use este enlace para citar
http://hdl.handle.net/2183/26664
A non ser que se indique outra cousa, a licenza do ítem descríbese como Atribución 4.0 Internacional
Coleccións
- CITEEC-CGM - Artigos [96]
Metadatos
Mostrar o rexistro completo do ítemTítulo
Evaluation of the Resilient Modulus of Hot-Mix Asphalt Made With Recycled Concrete Aggregates From Construction and Demolition WasteData
2020Cita bibliográfica
Galan, J.J.; Silva, L.M.; Pasandín, A.R.; Pérez, I. Evaluation of the Resilient Modulus of Hot-Mix Asphalt Made with Recycled Concrete Aggregates from Construction and Demolition Waste. Sustainability 2020, 12, 8551. https://doi.org/10.3390/su12208551
Resumo
[Abstract] This paper reports the influence of the percentage of recycled aggregate (RCA) from construction and demolition waste (C&DW) together with the percentage of binder (L), curing time (t) and temperature (T) of the samples on the stiffness of a hot asphalt mixture. The study was carried out using the response surface methodology (RSM). The resilient modulus was chosen to estimate the stiffness of the mixture. The percentages of RCA studied were 0% (control), 5%, 10%, 20% and 30%, whilst 3.5%, 4% and 4.5% were those chosen for the binder content. Before compacting the samples, they were left into the oven to cure. Curing time, or pretreatment time, were set at 0 (control), 2 and 4 h. The samples were subjected to temperatures of 0, 10 and 20 °C. The natural aggregate is of the hornfels type. All the specimens studied showed high stiffness at low temperatures. According to this research, temperature proved to be the most influential factor on the decrease in the resilient modulus and, conversely, the percentage of recycled aggregate is not a significant factor in the range of values studied.
Palabras chave
Recycled concrete aggregate
Construction and demolition waste
Resilient modulus
Hot-mix asphalt
Response surface methodology
Construction and demolition waste
Resilient modulus
Hot-mix asphalt
Response surface methodology