Skip navigation
  •  Inicio
  • UDC 
    • Cómo depositar
    • Políticas do RUC
    • FAQ
    • Dereitos de Autor
    • Máis información en INFOguías UDC
  • Percorrer 
    • Comunidades
    • Buscar por:
    • Data de publicación
    • Autor
    • Título
    • Materia
  • Axuda
    • español
    • Gallegan
    • English
  • Acceder
  •  Galego 
    • Español
    • Galego
    • English
  
Ver ítem 
  •   RUC
  • Escola Técnica Superior de Enxeñaría de Camiños, Canais e Portos
  • Investigación (ETSECCP)
  • Ver ítem
  •   RUC
  • Escola Técnica Superior de Enxeñaría de Camiños, Canais e Portos
  • Investigación (ETSECCP)
  • Ver ítem
JavaScript is disabled for your browser. Some features of this site may not work without it.

Fatigue Study of the Pre-Corroded 6082-T6 Aluminum Alloy in Saline Atmosphere

Thumbnail
Ver/abrir
metals-10-01260.pdf (2.364Mb)
Use este enlace para citar
http://hdl.handle.net/2183/26626
Atribución 4.0 Internacional
A non ser que se indique outra cousa, a licenza do ítem descríbese como Atribución 4.0 Internacional
Coleccións
  • Investigación (ETSECCP) [826]
Metadatos
Mostrar o rexistro completo do ítem
Título
Fatigue Study of the Pre-Corroded 6082-T6 Aluminum Alloy in Saline Atmosphere
Autor(es)
Fernández Muñoz, Alejandro
Mier, Jose
García-Diez, Ana
Camba, C.
Galán-Díaz, Juan José
Data
2020-09
Cita bibliográfica
Muñoz, A.F.; Buenhombre, J.L.M.; García-Diez, A.I.; Fabal, C.C.; Díaz, J.J.G. Fatigue Study of the Pre-Corroded 6082-T6 Aluminum Alloy in Saline Atmosphere. Metals 2020, 10, 1260. https://doi.org/10.3390/met10091260
Resumo
[Abstract] This work studies the influence of the saline atmospheric corrosion on the fatigue strength of 6061-T6 aluminum alloy. For this purpose, this alloy was subjected to tests in a salt spray corrosion chamber at different exposure times (1, 2, and 3 months) according to ASTM B117 standard. The morphological study of the pits was carried out by confocal microscopy. Subsequently, fatigue tests were performed at variable stresses whose maximum stress (Smax) was between 30% and 95% of the yield strength (S0) in order to keep them within the zone of elastic behavior of the material. Data were analyzed using the Basquin equation and the maximum likelihood function method. The results show a similar decrease in the conventional fatigue limit (2 × 106 cycles) after one month (98 MPa) and two months (91 MPa) of corrosion. After three months of corrosion, the material showed a very important reduction in the fatigue limit (68 MPa) with respect to the uncorroded material (131 MPa). The data of Se/S0 (fatigue limit/yield strength) versus the ratio Pm/Dm (pit average depth/pit diameter at zero depth) can be fitted to a logarithmic curve.
Palabras chave
Aluminio
Aleaciones
Corrosión
Metales
Fatiga
 
Versión do editor
https://doi.org/10.3390/met10091260
Dereitos
Atribución 4.0 Internacional
ISSN
2075-4701

Listar

Todo RUCComunidades e colecciónsPor data de publicaciónAutoresTítulosMateriasGrupo de InvestigaciónTitulaciónEsta colecciónPor data de publicaciónAutoresTítulosMateriasGrupo de InvestigaciónTitulación

A miña conta

AccederRexistro

Estatísticas

Ver Estatísticas de uso
Sherpa
OpenArchives
OAIster
Scholar Google
UNIVERSIDADE DA CORUÑA. Servizo de Biblioteca.    DSpace Software Copyright © 2002-2013 Duraspace - Suxestións