Synergistic Degradation Mechanism in Single Crystal Ni-Rich NMC//Graphite Cells
![Thumbnail](/dspace/bitstream/handle/2183/38635/Temprano_Farina_Israel_2023_Synergistic_Degradation_Mechanism_in_Single_Crystal_Ni-Rich_NMC_Graphite_Cells.pdf.jpg?sequence=4&isAllowed=y)
Use este enlace para citar
http://hdl.handle.net/2183/38635Coleccións
- GI-REACT! - Artigos [111]
Metadatos
Mostrar o rexistro completo do ítemTítulo
Synergistic Degradation Mechanism in Single Crystal Ni-Rich NMC//Graphite CellsData
2023-11-06Cita bibliográfica
ACS Energy Lett. 2023, 8, 5025−5031
Resumo
[Abstract]: Oxygen loss at high voltages in Ni-rich NMC//graphite Li-ion batteries promotes degradation, but increasing evidence from full cells reveals that the depth of discharge choice can further accelerate aging, i.e., synergistic degradation. In this Letter, we employ cycling protocols to examine the origin of the synergistic degradation for single crystal Ni-rich NMC//graphite pouch cells. In regimes where oxygen loss is not promoted (V < 4.3 V), a lower cutoff voltage does not affect capacity retention (after 100 cycles), despite significant graphite expansion occurring. In contrast, when NMC surface oxygen loss is induced (V > 4.3 V), deeper depth of discharge leads to pronounced faster aging. Using a combination of post-mortem analysis and density functional theory, we present a mechanistic description of surface phase densification and evolution as a function of voltage and cycling. The detrimental impact of this mechanism on lithium-ion kinetics is used to explain the observed cycling results.
Palabras chave
Degradation
Electrochemical cells
Electrodes
Oxides
Toxicological synergy
Electrochemical cells
Electrodes
Oxides
Toxicological synergy
Versión do editor
Dereitos
Copyright © 2023 The Authors. Published by American Chemical Society. This publication is licensed under CC-BY 4.0 (https://creativecommons.org/licenses/by/4.0/).
ISSN
2380-8195