Rodríguez-Martínez, XabierMartín, JaimeCampoy-Quiles, Mariano2025-12-102025-12-102024-06-25X. Rodríguez-Martínez, F. Saiz, B. Dörling, S. Marina, J. Guo, K. Xu, H. Chen, J. Martin, I. McCulloch, R. Rurali, J. S. Reparaz, M. Campoy-Quiles, On The Thermal Conductivity of Conjugated Polymers for Thermoelectrics. Adv. Energy Mater. 2024, 14, 2401705. https://doi.org/10.1002/aenm.2024017051614-6840https://hdl.handle.net/2183/46626[Abstract]: The thermal conductivity (κ) governs how heat propagates in a material, and thus is a key parameter that constrains the lifetime of optoelectronic devices and the performance of thermoelectrics (TEs). In organic electronics, understanding what determines κ has been elusive and experimentally challenging. Here, by measuring κ in 17 π-conjugated materials over different spatial directions, it is statistically shown how microstructure unlocks two markedly different thermal transport regimes. κ in long-range ordered polymers follows standard thermal transport theories: improved ordering implies higher κ and increased anisotropy. κ increases with stiffer backbones, higher molecular weights and heavier repeat units. Therein, charge and thermal transport go hand-in-hand and can be decoupled solely via the film texture, as supported by molecular dynamics simulations. In largely amorphous polymers, however, κ correlates negatively with the persistence length and the mass of the repeat unit, and thus an anomalous, albeit useful, behavior is found. Importantly, it is shown that for quasi-amorphous co-polymers (e.g., IDT-BT) κ decreases with increasing charge mobility, yielding a 10-fold enhancement of the TE figure-of-merit ZT compared to semi-crystalline counterparts (under comparable electrical conductivities). Finally, specific material design rules for high and low κ in organic semiconductors are provided.engAttribution 4.0 Internationalhttp://creativecommons.org/licenses/by/4.0/Conjugated polymersDesign rulesMolecular dynamicsOrganic thermoelectricsThermal anisotropyThermal conductivityjournal articleopen accesshttps://doi.org/10.1002/aenm.202401705