Laboratory and field performances of grave emulsion manufactured using nanocellulose crystals as an asphalt-emulsion emulsifier
Non accesible ata 2024-05-25
Use este enlace para citar
http://hdl.handle.net/2183/35935Coleccións
- CITEEC-CGM - Artigos [93]
Metadatos
Mostrar o rexistro completo do ítemTítulo
Laboratory and field performances of grave emulsion manufactured using nanocellulose crystals as an asphalt-emulsion emulsifierAutor(es)
Data
2023Cita bibliográfica
A.R. Pasandín, I. Pérez, F.J. Prego, A. Miguens (2024) Laboratory and field performances of grave emulsion manufactured using nanocellulose crystals as an asphalt-emulsion emulsifier, Road Materials and Pavement Design, 25:3, 492-510, DOI: 10.1080/14680629.2023.2216305
Resumo
[Abstract:] This research examines the feasibility of substituting commercial emulsifiers made by the chemical and petrochemical industries with nanocellulose. To achieve this, various bitumen emulsions are created using nanocellulose fibers and crystals as emulsifying agents. A grave-emulsion type GE-1 manufactured using bitumen emulsion produced with nanocellulose is studied. A control GE-1 is also tested. Modified proctor tests are employed to obtain the optimal fluid content; the optimum bitumen emulsion content is determined using an immersion-compression test. The compactability of GE-1 is analysed using a gyratory compactor. Finally, the moisture damage resistance (tensile strength ratio), stiffness (resilient modulus), and permanent deformation (repeated load axial test) are studied. A trial section constructed on a real scale. The cores are collected after one year and the stiffness is analysed. The results indicate that conventional emulsifying agents can be partially replaced with nanocellulose crystals in the manufacture of cationic slow-setting bituminous emulsions for grave emulsions.
Palabras chave
Nanocellulose crystals
Nanocellulose fibres
Emulsifier
Bitumen emulsion
Grave emulsion
Trial section
Nanocellulose fibres
Emulsifier
Bitumen emulsion
Grave emulsion
Trial section
Descrición
Versión aceptada de: https://doi.org/10.1080/14680629.2023.2216305