LiCo1−yMyO2 positive electrodes for rechargeable lithium batteries: II. Nickel substituted materials grown by the citrate method
Use este enlace para citar
http://hdl.handle.net/2183/14031Coleccións
- GI- Quimolmat - Artigos [110]
Metadatos
Mostrar o rexistro completo do ítemTítulo
LiCo1−yMyO2 positive electrodes for rechargeable lithium batteries: II. Nickel substituted materials grown by the citrate methodData
2006-03Cita bibliográfica
Julien CM, Amdouni A, Castro-Garcia S, Selmane M, Rangan S. LiCo1-yMyO2 positive electrodes for rechargeable lithium batteries: II. nickel substituted materials grown by the citrate method. Materials Science and Engineering B: Solid-State Materials for Advanced Technology 2006;128(1-3):138-50
Resumo
[Abstract] The layered LiCo1−yNiyO2 microcrystalline powders were synthesized by a sol–gel method using citric acid as a chelating agent in the range 0.2 ≤ y ≤ 0.8. Submicron-sized particles of the precursor were obtained at temperature below 400 °C and microcrystalline powders were grown by thermal treatment at 700 °C for 5 h in air. The carboxylic-based acid functioned such as a fuel, decomposed the homogeneous precipitate of metal complexes at low temperature, and yielded the free impurity LiCo1−yNiyO2 single-phases suitable for electrochemical applications. The synthesized products were characterized by structural, spectroscopic and thermal analyses. FT-IR measurements provide information on the growth process and the final local environment in the cationic sublattice of LiCo1−yNiyO2 solid solution. The electrochemical performance of the synthesized products in rechargeable Li cells was evaluated using non-aqueous solution 1 M LiPF6 in EC-DMC as electrolyte. The electrochemical features of a series of LiCo1−yNiyO2 compounds (0.2 ≤ y ≤ 1.0) are discussed in relation with their synthesis procedure and substitutive amount. The substitution of Ni3+ for Co3+ in LiCo1−yNiyO2 for y = 0.75 shows improvement of the specific capacity at ca. 187 mAh/g upon 32 cycles.
Palabras chave
Lithium nickel–cobalt oxides
Lithium diffusivity
Lithium secondary batteries
Citric acid
Chelating agent
Sol–gel method
Lithium diffusivity
Lithium secondary batteries
Citric acid
Chelating agent
Sol–gel method